Stainless Steel, 410

This grade is a Cr steel hardenable by heat treatment, which will attain high mechanical properties after heat treatment. It has good impact strength, corrosion and scaling resistance up to 1200 F (649 C). Applications are steam and gas turbine blades and buckets, bushings, valve components, fasteners, missile rocket components and medical instruments.

 

Chemical Composition (Weight %)
  C Mn Si P S Cr
Min

 

11.5
Max 0.15 0.50 1.00 0.04 0.03 13.5

Typical Mechanical Properties (Min)
Condition Tensile Strength, PSI Yield Strength 0.2%, PSI  Elongation %  Reduction of Area %  Hardness HB
A 115,000


241
HT 120,000 90,000 12 40 269 max
 

Related Specifications and Conditions

AMS-QQ-S-763, ASTM A479, ASTM A276, AMS5504, ASTM A182, UNS S41000, AMS5612, AMS5613, 1.4006

Available Forms 

Round bar, flat bar, hex bar, sheet, strip, plate, wire, coil, forgings
 
Chemical Composition (Weight %)
  Min Max
C   0.15
Mn   0.50
Si   1.00
P   0.04
S   0.03
Cr 11.5 13.5

Typical Mechanical Properties (Min)
Condition A
Tensile Strength, PSI 115,000
Yield Strength 0.2%, PSI  
 Elongation %  
 Reduction of Area %  
 Hardness HB 241
HT
Tensile Strength, PSI 120,000
Yield Strength 0.2%, PSI 90,000
 Elongation % 12
 Reduction of Area % 40
 Hardness HB 269 max
 

Related Specifications and Conditions

AMS-QQ-S-763, ASTM A479, ASTM A276, AMS5504, ASTM A182, UNS S41000, AMS5612, AMS5613, 1.4006

Available Forms 

Round bar, flat bar, hex bar, sheet, strip, plate, wire, coil, forgings